成钢.稀土Dy、退火对Dyx(Co40Ag60)100-x颗粒膜的结构与巨磁电阻效应的影响[J].工程科学与技术,2011,43(1):214-218.
Cheng Gang. Influence of Dy content and annealing temperature on the structure and giant magnetoresistance of Dyx(Co40Ag60)100-x granular films[J]. Advanced Engineering Sciences, 2011,43(1):214-218.
中文摘要: 采用磁控溅射法制备了Dyx(Co40Ag60)100-x颗粒膜。X射线衍射实验结果表明:Dyx(Co40Ag60)100-x颗粒膜的晶体结构具有一定的择优取向
退火温度升高能够促进这种择优取向并加速Ag颗粒的聚集生长和Ag中的Co发生相分离..稀土元素Dy起到细化晶粒的作用
并且阻碍晶面择优取向的进程
导致薄膜结构中的晶界增多从而引起薄膜电阻变大;巨磁电阻效应(GMR)测量结果表明:对所有不同成分薄膜样品当退火温度高于250℃时,GMR值是趋于减小的。由于掺杂稀土元素Dy会引起薄膜电阻的增大从而导致GMR效应减小的趋势,但少量的Dy元素(x=0.7)和适当的退火处理即能保持GMR效应的稳定性又能提高它对磁场的灵敏度,GMR和S的最大值分别为-18%和1.5×10-4 (A/m)-1。
Abstract:Dyx(Co40Ag60)100-x (x=0
0.7
1.4
2.1
2.8
3.5) granular films have been prepared by DC magneto controlled sputtering method. The XRD data indicated that Dyx(Co40Ag60)100-x films favors the (111) plane preferential orientation. The high annealing temperature t can promote the (111) plane of Ag preferential orientation and Co dissolving in Ag to separate from Ag and accelerate grain growing. Dy element plays the role of a grain refiner and retards the (111) plane preferential orientation result in increasing grains boundary and resistance of films. Magnetic measurements indicated that the value of GMR decreases of all films when annealing temperature is higher 250℃ because of increasing of resistance of films
but it can enhance sensitivityof films doped small Dy element. For small amount of addition Dy to CoAg granular films and proper heat treatment
Dy element can keep the value of GMR a constant and enhance sensitivity. Both maximum values of GMR and sensitivity are -18% and 1.5×10-4 (A/m)-1
respectively.
巨磁电阻效应颗粒膜磁性颗粒
Giant magnetoresistanceGranular filmsMagnetic particle
Yu R H;Zhang X X;Tejada J,Giant magnetoresistance in magnetic granular Co15Cu85 alloys annealed by directcurrent Joule heating,Journal of Magnetism and Magnetic Materials,1996(1-2).
Okano R;Takanashi K;Hono K Magnetoresistance and phase decomposition in Cr-Fe bulk alloys [J]
Ge Shihui;Zhang Zongzhi;Xu Tao Giant magnetoresistance and microstructure of Co-Cu and FeCo-Cu granular films [J]
Xiao Gang;Wang Jianqing;Xiong Peng Giant magnetoresistance and its evolution in the granular FexAg100-x system(0≤x≤100) [J]
de Azevedo, M.M. Pereira ;Kravetz, A.F. ;Amaral, V.S. ;Pogorelov, Yu.G. ;Sousa, J.B. ;Kakazei, G.N.,GMR in co-evaporated Co-Ag granular thin films,Journal of Magnetism and Magnetic Materials ,1999, 196/197(0).
严健生;沈鸿烈;沈勤我,CozAg100-x颗粒膜的巨磁电阻效应及其物理机制研,功能材料与器件学报,1998(1).
王长征,周宁,戎咏华.金属颗粒膜巨磁电阻效应的机制和影响因素[J].功能材料,2003(3)
BAIBICH M N;BROTO J M;FERT A,Giant magnetoresistance of (001) Fe/(001) Cr magnetic superlattices,Physical Review Letters
Malkinski L M;Wang J Q;Seip C T Thickness dependence of giant magnetoresistance effect in granular Cu-Co thin films [J]
Milner A;Gerber A;Groisman B Spin-dependent electronic transport in granular ferromagnets [J]
Xiao J Q;Jiang J S;Chien C L Giant magnetoresistance in nonmultilayer magnetic systems [J]
Berkowits A E;Mitekell J R;Corey M J,Giant magnetoresistance in heterogeneous Cu-Co alloys,Physical Review Letters,1992.
Wang, CZ ;Zhang, PM ;Zheng, LB ;Mao, XG ;Rong, YH,Influence of annealing on microstructure and magnetic-transport of FeCo-Al2O3 nanogranular films,Thin Solid Films ,2008, 516(10).
Hylton T L;Coffey K R;Parker M A,Giant magnetoresistance at low fields in discontinuous NiFe-Ag multilayer thin films,Science,1993(5 124).
Tiwari A;Senthil-Kumar M,Effect of addition of Ni on the structure and giant magnetoresistance in Fe-Co films,Physical Review B,2007(1-2).
Ping Sheng;Abeles B;Arie Y,Hopping conductivity in granular metals,Physical Review Letters,1973.
Tonooka K. ;Nishimura O.,Effect of rare-earth-doping on the magnetoresistive properties of sputtered Co-Ag alloy thin films,Applied Surface Science ,2001, 169(0).
0
浏览量
4
下载量
0
CNKI被引量
关联资源
相关文章
相关作者
相关机构
京公网安备11010802024621